Neutron diffraction analysis of a defect vanadium monoxide close to the equiatomic vanadium monoxide

Neutron and X-ray diffraction analyses are applied to studying the defect structure of synthesis-temperature quenched and low-temperature annealed vanadium monoxides VO _y (0.90 ≤ y ≤ 0.97) close to the equiatomic monoxide VO_1.0. It is found that the monoxides VO_0.90 and VO_0.97 contain structural vacancies not only in the oxygen sublattice, but also in the metal sublattice. In addition to the cubic disordered phase VO _y with the structure B1, the monoclinic superstructure V₁₄O₆ with space group C2/m is present in the synthesized VO_0.90 sample and in the annealed VO_0.90 and VO_0.97 samples. The formation of the V₁₄O₆ superstructure is attributed to the ordering of oxygen atoms and nonmetal vacancies in the lattice of the tetragonal solid solution of oxygen in vanadium. No simultaneous ordering of metal and oxygen vacancies in two sublattices of the cubic vanadium is observed.