Calcium-based coordination polymers from a solvothermal synthesis of HKUST-1 in 3D printed autoclaves

A mixed-metal 1D coordination polymer [CaCu(HBTC)₂(H2O)₈]_n (where H₃BTC – benzene-1,3,5-tric arboxylic acid) was obtained in a solvothermal synthesis of a well-known copper-containing metal–organic framework [Cu₃(BTC)₂(H₂O)₃]_n (HKUST-1) in autoclaves 3D-printed from commercial polypropylene. This material was a source of calcium ions, apparently, leaking from a colorant (calcium carbonate) promoted by glacial acetic acid as a modulator used to produce large single crystals of HKUST-1. This finding was confirmed by elemental analysis and a model experiment that resulted in a new calcium-based 1D coordination polymer [Ca(H₂BTC)₂(H₂O)₅]_n under the same solvothermal conditions with no copper or calcium salts put into a 3D-printed autoclave.